Material | Symbol | Unit | P1 | P2 | P3 | P4 | P5 | |
---|---|---|---|---|---|---|---|---|
Initial permeability | 25°C | µi | 2000 25% | 2500 25% | 2300 25% | 2200 25% | 1400 25% | |
Amplitude permeability at 25kHz sine wave,200mT |
25°C | µa | 2800min | 3200min | 3000min | 2800min | 2400min | |
Curie temperature | Tc | °C | >220 | >230 | >215 | >230 | >235 | |
Relative Core loss 25KHz200mT |
25°C | PV | kw/m³ | <165 | <130 | <120 | ||
60°C | <115 | <90 | <80 | |||||
100°C | <155 | <100 | <70 | |||||
Relative Core loss 100KHz200mT |
25°C | PV | kw/m³ | <650 | <600 | 130 | ||
60°C | <480 | <400 | 90 | |||||
100°C | <420 | <310 | 80 | |||||
Relative Core loss 300KHz100mT |
25°C | PV | kw/m³ | 670 | 230 | |||
60°C | 540 | 240 | ||||||
100°C | 480 | 260 | ||||||
Relative Core loss 500KHz50mT |
25°C | PV | 3kw/m³ | 310 | 180 | |||
60°C | 280 | 160 | ||||||
100°C | 250 | 120 | ||||||
Saturation flux density at 1000A/m f=10kHz |
25°C | Bms | MT | 470 | 510 | 500 | 490 | 470 |
60°C | 430 | 450 | 440 | 450 | 420 | |||
100°C | 370 | 390 | 380 | 400 | 380 | |||
Remanence | 25°C | Brms | MT | 130 | 118 | 95 | 130 | 130 |
60°C | 90 | 80 | 65 | 65 | 65 | |||
100°C | 95 | 83 | 55 | 60 | 55 | |||
Coercivity field strength f=10kHz |
25°C | Hc | A/m | 13 | 12 | 13 | 18 | 30 |
60°C | 8 | 8 | 10 | 16 | 30 | |||
100°C | 8 | 8 | 9 | 11 | 47.2 | |||
Resistvity | ρ | Ωm | 10 | 10 | 7 | 7 | 7 | |
Density | δ | g/cm³ | 4.8 | 4.8 | 4.8 | 4.8 | 4.8 | |
Note 1 | EI,EE,PQ, EER,RM, EP,EFD, EPC,EF, ETD,UI, EL,POT,T |
EI,EE,PQ, EER,RM, EP,EFD, EPC,EF, ETD,UI, EL,POT,T |
EI,EE,PQ, EER,RM, EP,EFD, EPC,EF, ETD,FEY POT,T,EPX EEM |
EI,EE,PQ, EER,RM, EP,EFD, EPC,EF, ETD,FEY POT,T,EPX EEM |
EI,EE,PQ, EER,RM, EP,EFD, EPC,EF, ETD,FEY POT,T,EPX EEM |